ICS 29.035.99
CCS K 15
GB/T 31034—2024
晶体硅太阳电池组件用绝缘背板
Insulating back sheet for crystalline silicon photovoltaic（PV） modules
2024⁃09⁃29 发布2025⁃04⁃01 实施
国家市场监督管理总局
国家标准化管理委员会发布
代替 GB/T 31034—2014
目 次
前言··························································································································Ⅲ
1 范围·······················································································································1
2 规范性引用文件········································································································1
3 术语和定义··············································································································2
4 分类·······················································································································2
5 要求·······················································································································2
6 试验方法·················································································································5
7 检验规则···············································································································11
8 标志、包装、运输和贮存·····························································································11
前 言
本文件按照GB/T 1.1—2020《标准化工作导则 第1 部分：标准化文件的结构和起草规则》的规
定起草。
本文件代替GB/T 31034—2014《晶体硅太阳电池组件用绝缘背板》，与GB/T 31034—2014 相比，
除结构调整和编辑性改动外，主要技术变化如下：
——增加了共挤型背板产品类型和性能要求（见第4 章、表1）；
——增加了“单位面积质量及允许偏差”“长期耐热性”“相比电痕化指数（CTI）”“绝缘穿透距离
（DTI）”“透光率”和“反射率”的性能要求（见表1）；
——将“系统最大电压”的要求按DC 1000 V 和DC 1500 V 进行区分（见表1，2014 年版的表1）；
—— 将紫外老化辐照剂量由“60 kWh/m2、45 kWh/m2 和30 kWh/m2”更改为“UV300 kWh/m2、
UV200 kWh/m2 和UV120 kWh/m2”（见表1，2014 年版的表3）；
——将“厚度”中“记录数据结果取中值并报告最小值”更改为“记录结果取平均值，精确到1 μm”
（见6.3，2014 年版的6.3）；
—— 删除了试验方法“ 水蒸气透过率”中电解传感器法的“ 优先选用该方法”的规定（2014 年版
的6.5.1）；
——将“拉伸强度和断裂伸长率”中拉伸速度由100 mm/min 更改为50 mm/min，将测试结果取中
值更改为取平均值（见6.8，2014 年版的6.6）；
——将“层间剥离强度[复合型]”、“背板/封装胶膜剥离强度”、“背板/硅胶剥离强度”和“耐紫外
（UV）老化性”中的测试结果取中值更改为取平均值（见6.9、6.11、6.12 和6.26，2014 年版的
6.7、6.9、6.10 和6.20）；
——增加了“耐湿热老化性”和“耐紫外（UV）老化性”中“击穿电压”和“断裂伸长率”相应试验要求
的试样尺寸和数量规定（见6.25、6.26）；
——删除了“耐磨性”中符合JTG E40—2007 和JTG E60—2008 要求的内容（2014 年版的6.23）。
请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。
本文件由中国电器工业协会提出。
本文件由全国绝缘材料标准化技术委员会（SAC/TC 51）归口。
本文件起草单位：苏州赛伍应用技术股份有限公司、通威太阳能（成都）有限公司、江苏中来新材科
技有限公司、晶澳太阳能科技股份有限公司、苏州固泰新材股份有限公司、桂林赛盟检测技术有限公
司、明冠新材料股份有限公司、桂林电器科学研究院有限公司、乐凯胶片股份有限公司、四川东材新材
料有限责任公司、江苏裕兴薄膜科技股份有限公司、广州宝力达电工材料有限公司、广东顺德大地缘新
材料有限公司、威凯检测技术有限公司、常州百佳年代薄膜科技股份有限公司、浙江中聚材料有限公
司、杭州和顺科技股份有限公司、无锡市检验检测认证研究院、隆基绿能科技股份有限公司、中节能太
阳能科技（镇江）有限公司、浙江晶科能源有限公司、中国建筑第二工程局有限公司、中国华能集团清洁
能源技术研究院有限公司、济南思克测试技术有限公司、中国计量大学、浙江爱旭太阳能科技有限公
司、上迈（镇江）新能源科技有限公司、深圳市运通天下科技有限公司、宿迁泰晶新材料科技有限公司、
杭州新子光电科技有限公司、杭州索日智能装备有限公司、江苏美科太阳能科技股份有限公司、中山市
CCS K 15
GB/T 31034—2024
晶体硅太阳电池组件用绝缘背板
Insulating back sheet for crystalline silicon photovoltaic（PV） modules
2024⁃09⁃29 发布2025⁃04⁃01 实施
国家市场监督管理总局
国家标准化管理委员会发布
代替 GB/T 31034—2014
目 次
前言··························································································································Ⅲ
1 范围·······················································································································1
2 规范性引用文件········································································································1
3 术语和定义··············································································································2
4 分类·······················································································································2
5 要求·······················································································································2
6 试验方法·················································································································5
7 检验规则···············································································································11
8 标志、包装、运输和贮存·····························································································11
前 言
本文件按照GB/T 1.1—2020《标准化工作导则 第1 部分：标准化文件的结构和起草规则》的规
定起草。
本文件代替GB/T 31034—2014《晶体硅太阳电池组件用绝缘背板》，与GB/T 31034—2014 相比，
除结构调整和编辑性改动外，主要技术变化如下：
——增加了共挤型背板产品类型和性能要求（见第4 章、表1）；
——增加了“单位面积质量及允许偏差”“长期耐热性”“相比电痕化指数（CTI）”“绝缘穿透距离
（DTI）”“透光率”和“反射率”的性能要求（见表1）；
——将“系统最大电压”的要求按DC 1000 V 和DC 1500 V 进行区分（见表1，2014 年版的表1）；
—— 将紫外老化辐照剂量由“60 kWh/m2、45 kWh/m2 和30 kWh/m2”更改为“UV300 kWh/m2、
UV200 kWh/m2 和UV120 kWh/m2”（见表1，2014 年版的表3）；
——将“厚度”中“记录数据结果取中值并报告最小值”更改为“记录结果取平均值，精确到1 μm”
（见6.3，2014 年版的6.3）；
—— 删除了试验方法“ 水蒸气透过率”中电解传感器法的“ 优先选用该方法”的规定（2014 年版
的6.5.1）；
——将“拉伸强度和断裂伸长率”中拉伸速度由100 mm/min 更改为50 mm/min，将测试结果取中
值更改为取平均值（见6.8，2014 年版的6.6）；
——将“层间剥离强度[复合型]”、“背板/封装胶膜剥离强度”、“背板/硅胶剥离强度”和“耐紫外
（UV）老化性”中的测试结果取中值更改为取平均值（见6.9、6.11、6.12 和6.26，2014 年版的
6.7、6.9、6.10 和6.20）；
——增加了“耐湿热老化性”和“耐紫外（UV）老化性”中“击穿电压”和“断裂伸长率”相应试验要求
的试样尺寸和数量规定（见6.25、6.26）；
——删除了“耐磨性”中符合JTG E40—2007 和JTG E60—2008 要求的内容（2014 年版的6.23）。
请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。
本文件由中国电器工业协会提出。
本文件由全国绝缘材料标准化技术委员会（SAC/TC 51）归口。
本文件起草单位：苏州赛伍应用技术股份有限公司、通威太阳能（成都）有限公司、江苏中来新材科
技有限公司、晶澳太阳能科技股份有限公司、苏州固泰新材股份有限公司、桂林赛盟检测技术有限公
司、明冠新材料股份有限公司、桂林电器科学研究院有限公司、乐凯胶片股份有限公司、四川东材新材
料有限责任公司、江苏裕兴薄膜科技股份有限公司、广州宝力达电工材料有限公司、广东顺德大地缘新
材料有限公司、威凯检测技术有限公司、常州百佳年代薄膜科技股份有限公司、浙江中聚材料有限公
司、杭州和顺科技股份有限公司、无锡市检验检测认证研究院、隆基绿能科技股份有限公司、中节能太
阳能科技（镇江）有限公司、浙江晶科能源有限公司、中国建筑第二工程局有限公司、中国华能集团清洁
能源技术研究院有限公司、济南思克测试技术有限公司、中国计量大学、浙江爱旭太阳能科技有限公
司、上迈（镇江）新能源科技有限公司、深圳市运通天下科技有限公司、宿迁泰晶新材料科技有限公司、
杭州新子光电科技有限公司、杭州索日智能装备有限公司、江苏美科太阳能科技股份有限公司、中山市